| Pressure resistance strength 470N/mm2 Density 8.8g/cm3 |
| Coefficient of heat conduction 58W/m.K Linear expansion coefficient 18.5x10/k |
| Alloy hardness 90-120HB Elongation 40% |
| Alloy material CuSn8P |
The product is improved from 090.The hole is arranged on the surface according to certain angle and density. It can delay life, low lubricating frequency and decrease wear, etc.
Pressure resistance strength 470N/mm² Density 8.8g/cm³
Coefficient of heat conduction 58W/m.K Linear expansion coefficient 18.5×10 /k
Alloy hardness 90~120HB Elongation 40%
Alloy material CuSn8P
The advantages of FB090 series products are:
1. Saving large amount of bronze material and save the working hours normally spent for lathing the bronze bushing.
2. Compared with lathed bushings and roller bearings, it is lights and more cost-effective.
3. Various holes and dents can be made on the frication surface for grease storage, prolonging the lubrication interval to 5 times as long as required by the bronze bushing.
4. Extremely high load sustainability, especially suitable for coarse abrasion surfaces.
Standaed products available: Straight bushings, thrust plates and pressure bearings.
Non-standard products available: Straight bushings, thrust plates, planks, bearing bushings, slide plates and steel bushing assembly.
FB090 Series bearings are widely used in applications sush as agricultural machineries, construction machineries, engineering machineries and automobile industry.
| Pressure resistance strength 470N/mm2 Density 8.8g/cm3 |
| Coefficient of heat conduction 58W/m.K Linear expansion coefficient 18.5x10/k |
| Alloy hardness 90-120HB Elongation 40% |
| Alloy material CuSn8P |
The product is improved from 090.The hole is arranged on the surface according to certain angle and density. It can delay life, low lubricating frequency and decrease wear, etc.
Pressure resistance strength 470N/mm² Density 8.8g/cm³
Coefficient of heat conduction 58W/m.K Linear expansion coefficient 18.5×10 /k
Alloy hardness 90~120HB Elongation 40%
Alloy material CuSn8P
The advantages of FB090 series products are:
1. Saving large amount of bronze material and save the working hours normally spent for lathing the bronze bushing.
2. Compared with lathed bushings and roller bearings, it is lights and more cost-effective.
3. Various holes and dents can be made on the frication surface for grease storage, prolonging the lubrication interval to 5 times as long as required by the bronze bushing.
4. Extremely high load sustainability, especially suitable for coarse abrasion surfaces.
Standaed products available: Straight bushings, thrust plates and pressure bearings.
Non-standard products available: Straight bushings, thrust plates, planks, bearing bushings, slide plates and steel bushing assembly.
FB090 Series bearings are widely used in applications sush as agricultural machineries, construction machineries, engineering machineries and automobile industry.
PVC Resin
PVC Resin is easy to process, and can be processed by molding, lamination, injection molding, extrusion, calendering, blow molding and other hollow methods. Polyvinyl chloride is mainly used to produce artificial leather, film, wire sheath and other plastic soft products, but also can produce plates, doors and windows, pipes and valves and other plastic hard products.
PVC Resin usually inculde carbide based and ethylene based. K66-K68 PVC RESIN, K59-K55 PVC RESIN, K71-K73 PVC RESIN. PVC RESIN SG5, PVC RESIN SG3, PVC RESIN SG8.
According to the different application scope, PVC can be divided into: general-purpose PVC resin, high polymerization degree PVC resin, and cross-linked PVC resin. General-purpose PVC resin is formed by the polymerization of vinyl chloride monomer under the action of initiator; high degree of polymerization PVC resin refers to the resin polymerized by adding chain extender to the vinyl chloride monomer polymerization system; cross-linked PVC resin is A resin polymerized by adding a crosslinking agent containing diene and polyene to the vinyl chloride monomer polymerization system.
According to the method of obtaining vinyl chloride monomer, it can be divided into Calcium Carbide method, ethylene method and imported (EDC, VCM) monomer method (the ethylene method and imported monomer method are commonly referred to as ethylene method).
According to the polymerization method, polyvinyl chloride can be divided into four categories: suspension polyvinyl chloride, emulsion polyvinyl chloride, bulk polyvinyl chloride, and solution polyvinyl chloride. Suspension process polyvinyl chloride is the largest variety in output, accounting for about 80% of the total output of PVC. Suspension method PVC is divided into six models according to absolute viscosity: XS-1, XS-2--XS-6; XJ-1, XJ-2--, XJ-6. The meaning of each letter in the model: X-suspension method; S-loose type; J-compact type.
Pvc Resin,Pvc Resin Powder,Pvc Resin Sg5,Pvc Resin K67
Henan Shunbang Chemical Industry CO.,Ltd , https://www.suspensionpvc.com